C67600 Bronze vs. C15500 Copper
Both C67600 bronze and C15500 copper are copper alloys. They have 59% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C67600 bronze and the bottom bar is C15500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 13 to 33 | |
| 3.0 to 37 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 43 |
| Shear Strength, MPa | 270 to 350 | |
| 190 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 570 | |
| 280 to 550 |
| Tensile Strength: Yield (Proof), MPa | 170 to 380 | |
| 130 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 890 | |
| 1080 |
| Melting Onset (Solidus), °C | 870 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 350 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 90 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 91 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 33 |
| Density, g/cm3 | 8.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 47 | |
| 42 |
| Embodied Water, L/kg | 330 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 to 130 | |
| 15 to 84 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 680 | |
| 72 to 1210 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 8.6 to 17 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 11 to 17 |
| Thermal Diffusivity, mm2/s | 35 | |
| 100 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 9.8 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 57 to 60 | |
| 99.75 to 99.853 |
| Iron (Fe), % | 0.4 to 1.3 | |
| 0 |
| Lead (Pb), % | 0.5 to 1.0 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0.080 to 0.13 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.040 to 0.080 |
| Silver (Ag), % | 0 | |
| 0.027 to 0.1 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0 |
| Zinc (Zn), % | 35.2 to 41.6 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.2 |