C68000 Brass vs. Grade 361 Molybdenum
C68000 brass belongs to the copper alloys classification, while grade 361 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C68000 brass and the bottom bar is grade 361 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 310 |
| Elongation at Break, % | 27 | |
| 6.3 |
| Poisson's Ratio | 0.3 | |
| 0.31 |
| Shear Modulus, GPa | 40 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 390 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 250 |
| Thermal Expansion, µm/m-K | 21 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 28 |
| Embodied Energy, MJ/kg | 48 | |
| 330 |
| Embodied Water, L/kg | 330 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 | |
| 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 | |
| 450 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 17 |
| Stiffness to Weight: Bending, points | 20 | |
| 22 |
| Strength to Weight: Axial, points | 14 | |
| 17 |
| Strength to Weight: Bending, points | 15 | |
| 16 |
| Thermal Shock Resistance, points | 13 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 56 to 60 | |
| 0 |
| Iron (Fe), % | 0.25 to 1.3 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0.010 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 99.9 to 100 |
| Nickel (Ni), % | 0.2 to 0.8 | |
| 0 to 0.0050 |
| Nitrogen (N), % | 0 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0070 |
| Silicon (Si), % | 0.040 to 0.15 | |
| 0 to 0.010 |
| Tin (Sn), % | 0.75 to 1.1 | |
| 0 |
| Zinc (Zn), % | 35.6 to 42.8 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |