C68400 Brass vs. CC481K Bronze
Both C68400 brass and CC481K bronze are copper alloys. They have 62% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C68400 brass and the bottom bar is CC481K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 | |
| 90 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 18 | |
| 4.5 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 41 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 350 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 170 |
| Melting Completion (Liquidus), °C | 840 | |
| 1000 |
| Melting Onset (Solidus), °C | 820 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 370 |
| Thermal Conductivity, W/m-K | 66 | |
| 64 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 87 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 35 |
| Density, g/cm3 | 7.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.7 |
| Embodied Energy, MJ/kg | 47 | |
| 60 |
| Embodied Water, L/kg | 320 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 | |
| 13 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 | |
| 150 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 19 | |
| 11 |
| Strength to Weight: Bending, points | 19 | |
| 13 |
| Thermal Diffusivity, mm2/s | 21 | |
| 20 |
| Thermal Shock Resistance, points | 18 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.5 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.050 |
| Boron (B), % | 0.0010 to 0.030 | |
| 0 |
| Copper (Cu), % | 59 to 64 | |
| 87 to 89.5 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0.2 to 1.5 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0.030 to 0.3 | |
| 0 to 1.0 |
| Silicon (Si), % | 1.5 to 2.5 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 to 0.5 | |
| 10 to 11.5 |
| Zinc (Zn), % | 28.6 to 39.3 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 |