C68800 Brass vs. R31537 Cobalt
C68800 brass belongs to the copper alloys classification, while R31537 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C68800 brass and the bottom bar is R31537 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 220 |
| Elongation at Break, % | 2.0 to 36 | |
| 14 to 23 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 41 | |
| 87 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 890 | |
| 1000 to 1340 |
| Tensile Strength: Yield (Proof), MPa | 390 to 790 | |
| 590 to 940 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 320 |
| Melting Completion (Liquidus), °C | 960 | |
| 1360 |
| Melting Onset (Solidus), °C | 950 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 450 |
| Thermal Conductivity, W/m-K | 40 | |
| 13 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 20 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 8.1 |
| Embodied Energy, MJ/kg | 48 | |
| 110 |
| Embodied Water, L/kg | 350 | |
| 530 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 180 | |
| 140 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 710 to 2860 | |
| 780 to 1990 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 15 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 30 | |
| 33 to 44 |
| Strength to Weight: Bending, points | 19 to 25 | |
| 26 to 32 |
| Thermal Diffusivity, mm2/s | 12 | |
| 3.4 |
| Thermal Shock Resistance, points | 19 to 30 | |
| 24 to 32 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 3.0 to 3.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.14 |
| Chromium (Cr), % | 0 | |
| 26 to 30 |
| Cobalt (Co), % | 0.25 to 0.55 | |
| 58.9 to 69 |
| Copper (Cu), % | 70.8 to 75.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.75 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 5.0 to 7.0 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Zinc (Zn), % | 21.3 to 24.1 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |