C69300 Brass vs. AWS ENiCu-7
C69300 brass belongs to the copper alloys classification, while AWS ENiCu-7 belongs to the nickel alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C69300 brass and the bottom bar is AWS ENiCu-7.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 160 |
| Elongation at Break, % | 8.5 to 15 | |
| 34 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 41 | |
| 62 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 630 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 280 |
| Melting Completion (Liquidus), °C | 880 | |
| 1270 |
| Melting Onset (Solidus), °C | 860 | |
| 1230 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 430 |
| Thermal Conductivity, W/m-K | 38 | |
| 21 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 3.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 50 |
| Density, g/cm3 | 8.2 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 8.0 |
| Embodied Energy, MJ/kg | 45 | |
| 110 |
| Embodied Water, L/kg | 310 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 10 |
| Stiffness to Weight: Bending, points | 19 | |
| 21 |
| Strength to Weight: Axial, points | 19 to 21 | |
| 17 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 17 |
| Thermal Diffusivity, mm2/s | 12 | |
| 5.5 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.75 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 73 to 77 | |
| 20.6 to 38 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 2.5 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 4.0 |
| Nickel (Ni), % | 0 to 0.1 | |
| 62 to 69 |
| Phosphorus (P), % | 0.040 to 0.15 | |
| 0 to 0.020 |
| Silicon (Si), % | 2.7 to 3.4 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 1.0 |
| Zinc (Zn), % | 18.4 to 24.3 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |