C69300 Brass vs. C19500 Copper
Both C69300 brass and C19500 copper are copper alloys. They have 75% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C69300 brass and the bottom bar is C19500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 8.5 to 15 | |
| 2.3 to 38 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Rockwell B Hardness | 84 to 88 | |
| 71 to 86 |
| Shear Modulus, GPa | 41 | |
| 44 |
| Shear Strength, MPa | 330 to 370 | |
| 260 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 630 | |
| 380 to 640 |
| Tensile Strength: Yield (Proof), MPa | 300 to 390 | |
| 120 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 200 |
| Melting Completion (Liquidus), °C | 880 | |
| 1090 |
| Melting Onset (Solidus), °C | 860 | |
| 1090 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 38 | |
| 200 |
| Thermal Expansion, µm/m-K | 19 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 50 to 56 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 50 to 57 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 31 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 45 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 to 70 | |
| 14 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 700 | |
| 59 to 1530 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 19 to 21 | |
| 12 to 20 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 58 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 13 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Cobalt (Co), % | 0 | |
| 0.3 to 1.3 |
| Copper (Cu), % | 73 to 77 | |
| 94.9 to 98.6 |
| Iron (Fe), % | 0 to 0.1 | |
| 1.0 to 2.0 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0.040 to 0.15 | |
| 0.010 to 0.35 |
| Silicon (Si), % | 2.7 to 3.4 | |
| 0 |
| Tin (Sn), % | 0 to 0.2 | |
| 0.1 to 1.0 |
| Zinc (Zn), % | 18.4 to 24.3 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.2 |