C69300 Brass vs. C34200 Brass
Both C69300 brass and C34200 brass are copper alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C69300 brass and the bottom bar is C34200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 8.5 to 15 | |
| 3.0 to 17 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Rockwell B Hardness | 84 to 88 | |
| 53 to 91 |
| Shear Modulus, GPa | 41 | |
| 40 |
| Shear Strength, MPa | 330 to 370 | |
| 230 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 630 | |
| 370 to 650 |
| Tensile Strength: Yield (Proof), MPa | 300 to 390 | |
| 150 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 120 |
| Melting Completion (Liquidus), °C | 880 | |
| 910 |
| Melting Onset (Solidus), °C | 860 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 380 |
| Thermal Conductivity, W/m-K | 38 | |
| 120 |
| Thermal Expansion, µm/m-K | 19 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 24 |
| Density, g/cm3 | 8.2 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 45 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 to 70 | |
| 9.0 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 700 | |
| 110 to 870 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 19 to 21 | |
| 13 to 22 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 14 to 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 37 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 12 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 73 to 77 | |
| 62 to 65 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.090 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0.040 to 0.15 | |
| 0 |
| Silicon (Si), % | 2.7 to 3.4 | |
| 0 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 18.4 to 24.3 | |
| 32 to 36.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.4 |