C69300 Brass vs. C82800 Copper
Both C69300 brass and C82800 copper are copper alloys. They have 76% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C69300 brass and the bottom bar is C82800 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 8.5 to 15 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Rockwell B Hardness | 84 to 88 | |
| 45 to 85 |
| Shear Modulus, GPa | 41 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 630 | |
| 670 to 1140 |
| Tensile Strength: Yield (Proof), MPa | 300 to 390 | |
| 380 to 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 310 |
| Melting Completion (Liquidus), °C | 880 | |
| 930 |
| Melting Onset (Solidus), °C | 860 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 38 | |
| 120 |
| Thermal Expansion, µm/m-K | 19 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 12 |
| Embodied Energy, MJ/kg | 45 | |
| 190 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 to 70 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 700 | |
| 590 to 4080 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 19 to 21 | |
| 21 to 36 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 12 | |
| 36 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 23 to 39 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 2.5 to 2.9 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.15 to 0.7 |
| Copper (Cu), % | 73 to 77 | |
| 94.6 to 97.2 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.1 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0.040 to 0.15 | |
| 0 |
| Silicon (Si), % | 2.7 to 3.4 | |
| 0.2 to 0.35 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.12 |
| Zinc (Zn), % | 18.4 to 24.3 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |