C69700 Brass vs. Solder Alloy 601

C69700 brass belongs to the copper alloys classification, while solder alloy 601 belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is C69700 brass and the bottom bar is solder alloy 601.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
31
Elongation at Break, % 25
83
Poisson's Ratio 0.32
0.41
Shear Modulus, GPa 41
11
Tensile Strength: Ultimate (UTS), MPa 470
12

Thermal Properties

Latent Heat of Fusion, J/g 240
43
Melting Completion (Liquidus), °C 930
120
Melting Onset (Solidus), °C 880
120
Specific Heat Capacity, J/kg-K 400
230
Thermal Conductivity, W/m-K 43
34
Thermal Expansion, µm/m-K 19
23

Otherwise Unclassified Properties

Density, g/cm3 8.3
7.3
Embodied Water, L/kg 310
1330

Common Calculations

Stiffness to Weight: Axial, points 7.3
2.3
Stiffness to Weight: Bending, points 19
14
Strength to Weight: Axial, points 16
0.45
Strength to Weight: Bending, points 16
1.6
Thermal Diffusivity, mm2/s 13
20
Thermal Shock Resistance, points 16
1.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 75 to 80
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
51 to 52.5
Iron (Fe), % 0 to 0.2
0 to 0.020
Lead (Pb), % 0.5 to 1.5
0 to 0.070
Manganese (Mn), % 0 to 0.4
0
Nickel (Ni), % 0
0 to 0.010
Silicon (Si), % 2.5 to 3.5
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
47.5 to 48.5
Zinc (Zn), % 13.9 to 22
0 to 0.0010
Residuals, % 0 to 0.5
0