C70260 Copper vs. Class 2 Tungsten
C70260 copper belongs to the copper alloys classification, while class 2 tungsten belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C70260 copper and the bottom bar is class 2 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 260 |
| Elongation at Break, % | 9.5 to 19 | |
| 5.7 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 44 | |
| 100 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 760 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 410 to 650 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 120 |
| Thermal Conductivity, W/m-K | 160 | |
| 20 |
| Thermal Expansion, µm/m-K | 17 | |
| 4.6 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 to 50 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 40 to 51 | |
| 7.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 23 |
| Embodied Energy, MJ/kg | 43 | |
| 350 |
| Embodied Water, L/kg | 310 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 46 to 140 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 710 to 1810 | |
| 640 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 18 | |
| 14 |
| Strength to Weight: Axial, points | 16 to 24 | |
| 16 |
| Strength to Weight: Bending, points | 16 to 21 | |
| 13 |
| Thermal Diffusivity, mm2/s | 45 | |
| 11 |
| Thermal Shock Resistance, points | 18 to 27 | |
| 52 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 95.8 to 98.8 | |
| 0 |
| Nickel (Ni), % | 1.0 to 3.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.7 | |
| 0 |
| Tungsten (W), % | 0 | |
| 92.5 |
| Residuals, % | 0 to 0.5 | |
| 7.5 |