C70260 Copper vs. C17500 Copper
Both C70260 copper and C17500 copper are copper alloys. They have a very high 97% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C70260 copper and the bottom bar is C17500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 9.5 to 19 | |
| 6.0 to 30 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 45 |
| Shear Strength, MPa | 320 to 450 | |
| 200 to 520 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 760 | |
| 310 to 860 |
| Tensile Strength: Yield (Proof), MPa | 410 to 650 | |
| 170 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 220 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1060 |
| Melting Onset (Solidus), °C | 1040 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 160 | |
| 200 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 to 50 | |
| 24 to 53 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 40 to 51 | |
| 24 to 54 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 60 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 4.7 |
| Embodied Energy, MJ/kg | 43 | |
| 73 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 46 to 140 | |
| 30 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 710 to 1810 | |
| 120 to 2390 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 16 to 24 | |
| 9.7 to 27 |
| Strength to Weight: Bending, points | 16 to 21 | |
| 11 to 23 |
| Thermal Diffusivity, mm2/s | 45 | |
| 59 |
| Thermal Shock Resistance, points | 18 to 27 | |
| 11 to 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Beryllium (Be), % | 0 | |
| 0.4 to 0.7 |
| Cobalt (Co), % | 0 | |
| 2.4 to 2.7 |
| Copper (Cu), % | 95.8 to 98.8 | |
| 95.6 to 97.2 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 1.0 to 3.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.7 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |