C70400 Copper-nickel vs. C17000 Copper
Both C70400 copper-nickel and C17000 copper are copper alloys. They have a moderately high 93% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C70400 copper-nickel and the bottom bar is C17000 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 45 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 310 | |
| 490 to 1310 |
| Tensile Strength: Yield (Proof), MPa | 95 to 230 | |
| 160 to 1140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 270 |
| Melting Completion (Liquidus), °C | 1120 | |
| 980 |
| Melting Onset (Solidus), °C | 1060 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 64 | |
| 110 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 8.7 |
| Embodied Energy, MJ/kg | 47 | |
| 140 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 38 to 220 | |
| 110 to 5420 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 9.3 to 9.8 | |
| 15 to 41 |
| Strength to Weight: Bending, points | 11 to 12 | |
| 16 to 30 |
| Thermal Diffusivity, mm2/s | 18 | |
| 32 |
| Thermal Shock Resistance, points | 10 to 11 | |
| 17 to 45 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Beryllium (Be), % | 0 | |
| 1.6 to 1.8 |
| Copper (Cu), % | 89.8 to 93.6 | |
| 96.3 to 98.2 |
| Iron (Fe), % | 1.3 to 1.7 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0 |
| Nickel (Ni), % | 4.8 to 6.2 | |
| 0.2 to 0.6 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |