C70600 Copper-nickel vs. EN 1.4419 Stainless Steel
C70600 copper-nickel belongs to the copper alloys classification, while EN 1.4419 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C70600 copper-nickel and the bottom bar is EN 1.4419 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 3.0 to 34 | |
| 11 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 46 | |
| 76 |
| Shear Strength, MPa | 190 to 330 | |
| 410 to 950 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 570 | |
| 660 to 1590 |
| Tensile Strength: Yield (Proof), MPa | 63 to 270 | |
| 370 to 1240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 790 |
| Melting Completion (Liquidus), °C | 1150 | |
| 1440 |
| Melting Onset (Solidus), °C | 1100 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 44 | |
| 30 |
| Thermal Expansion, µm/m-K | 17 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.8 | |
| 2.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.9 | |
| 3.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 8.0 |
| Density, g/cm3 | 8.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.2 |
| Embodied Energy, MJ/kg | 51 | |
| 30 |
| Embodied Water, L/kg | 300 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.5 to 160 | |
| 95 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 16 to 290 | |
| 350 to 3920 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 9.1 to 18 | |
| 24 to 57 |
| Strength to Weight: Bending, points | 11 to 17 | |
| 22 to 39 |
| Thermal Diffusivity, mm2/s | 13 | |
| 8.1 |
| Thermal Shock Resistance, points | 9.8 to 19 | |
| 23 to 55 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.36 to 0.42 |
| Chromium (Cr), % | 0 | |
| 13 to 14.5 |
| Copper (Cu), % | 84.7 to 90 | |
| 0 |
| Iron (Fe), % | 1.0 to 1.8 | |
| 82 to 86 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.6 to 1.0 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |