C71500 Copper-nickel vs. CR014A Copper
Both C71500 copper-nickel and CR014A copper are copper alloys. They have 67% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C71500 copper-nickel and the bottom bar is CR014A copper.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
120 |
Poisson's Ratio | 0.33 | |
0.34 |
Shear Modulus, GPa | 52 | |
43 |
Tensile Strength: Ultimate (UTS), MPa | 380 to 620 | |
230 |
Thermal Properties
Latent Heat of Fusion, J/g | 230 | |
210 |
Maximum Temperature: Mechanical, °C | 260 | |
200 |
Melting Completion (Liquidus), °C | 1240 | |
1090 |
Melting Onset (Solidus), °C | 1170 | |
1040 |
Specific Heat Capacity, J/kg-K | 400 | |
390 |
Thermal Conductivity, W/m-K | 28 | |
380 |
Thermal Expansion, µm/m-K | 16 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 4.6 | |
98 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 4.7 | |
99 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 41 | |
32 |
Density, g/cm3 | 8.9 | |
9.0 |
Embodied Carbon, kg CO2/kg material | 5.1 | |
2.6 |
Embodied Energy, MJ/kg | 74 | |
42 |
Embodied Water, L/kg | 280 | |
340 |
Common Calculations
Stiffness to Weight: Axial, points | 8.6 | |
7.2 |
Stiffness to Weight: Bending, points | 19 | |
18 |
Strength to Weight: Axial, points | 12 to 19 | |
7.1 |
Strength to Weight: Bending, points | 13 to 18 | |
9.3 |
Thermal Diffusivity, mm2/s | 7.7 | |
110 |
Thermal Shock Resistance, points | 12 to 20 | |
8.1 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Bismuth (Bi), % | 0 | |
0 to 0.00050 |
Copper (Cu), % | 63.5 to 70.6 | |
99.913 to 99.969 |
Iron (Fe), % | 0.4 to 1.0 | |
0 |
Lead (Pb), % | 0 to 0.050 | |
0 |
Manganese (Mn), % | 0 to 1.0 | |
0 |
Nickel (Ni), % | 29 to 33 | |
0 |
Phosphorus (P), % | 0 | |
0.0010 to 0.0070 |
Silver (Ag), % | 0 | |
0.030 to 0.050 |
Zinc (Zn), % | 0 to 1.0 | |
0 |
Residuals, % | 0 to 0.5 | |
0 |