C71500 Copper-nickel vs. C66900 Brass
Both C71500 copper-nickel and C66900 brass are copper alloys. They have 65% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C71500 copper-nickel and the bottom bar is C66900 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Rockwell B Hardness | 40 to 89 | |
| 65 to 100 |
| Shear Modulus, GPa | 52 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 620 | |
| 460 to 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 260 | |
| 150 |
| Melting Completion (Liquidus), °C | 1240 | |
| 860 |
| Melting Onset (Solidus), °C | 1170 | |
| 850 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 400 |
| Thermal Expansion, µm/m-K | 16 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.6 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.7 | |
| 3.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 41 | |
| 23 |
| Density, g/cm3 | 8.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 2.8 |
| Embodied Energy, MJ/kg | 74 | |
| 46 |
| Embodied Water, L/kg | 280 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.6 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 15 to 26 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 16 to 23 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 14 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 63.5 to 70.6 | |
| 62.5 to 64.5 |
| Iron (Fe), % | 0.4 to 1.0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 11.5 to 12.5 |
| Nickel (Ni), % | 29 to 33 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 22.5 to 26 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.2 |