C71520 Copper-nickel vs. EN 1.4301 Stainless Steel
C71520 copper-nickel belongs to the copper alloys classification, while EN 1.4301 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C71520 copper-nickel and the bottom bar is EN 1.4301 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 10 to 45 | |
| 14 to 46 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 51 | |
| 77 |
| Shear Strength, MPa | 250 to 340 | |
| 430 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 570 | |
| 610 to 900 |
| Tensile Strength: Yield (Proof), MPa | 140 to 430 | |
| 220 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 260 | |
| 940 |
| Melting Completion (Liquidus), °C | 1170 | |
| 1430 |
| Melting Onset (Solidus), °C | 1120 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 480 |
| Thermal Conductivity, W/m-K | 32 | |
| 15 |
| Thermal Expansion, µm/m-K | 15 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.7 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.8 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 15 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.0 | |
| 3.0 |
| Embodied Energy, MJ/kg | 73 | |
| 43 |
| Embodied Water, L/kg | 280 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 54 to 130 | |
| 110 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 67 to 680 | |
| 120 to 820 |
| Stiffness to Weight: Axial, points | 8.6 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 18 | |
| 22 to 32 |
| Strength to Weight: Bending, points | 13 to 17 | |
| 20 to 27 |
| Thermal Diffusivity, mm2/s | 8.9 | |
| 4.0 |
| Thermal Shock Resistance, points | 12 to 19 | |
| 14 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.070 |
| Chromium (Cr), % | 0 | |
| 17.5 to 19.5 |
| Copper (Cu), % | 65 to 71.6 | |
| 0 |
| Iron (Fe), % | 0.4 to 1.0 | |
| 66.8 to 74.5 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 28 to 33 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |