C71640 Copper-nickel vs. CR003A Copper

Both C71640 copper-nickel and CR003A copper are copper alloys. They have 65% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C71640 copper-nickel and the bottom bar is CR003A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
120
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 52
43
Tensile Strength: Ultimate (UTS), MPa 490 to 630
230
Tensile Strength: Yield (Proof), MPa 190 to 460
140

Thermal Properties

Latent Heat of Fusion, J/g 240
210
Maximum Temperature: Mechanical, °C 260
200
Melting Completion (Liquidus), °C 1180
1090
Melting Onset (Solidus), °C 1120
1040
Specific Heat Capacity, J/kg-K 410
390
Thermal Conductivity, W/m-K 29
380
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
100
Electrical Conductivity: Equal Weight (Specific), % IACS 7.1
100

Otherwise Unclassified Properties

Base Metal Price, % relative 40
31
Density, g/cm3 8.9
9.0
Embodied Carbon, kg CO2/kg material 5.0
2.6
Embodied Energy, MJ/kg 73
41
Embodied Water, L/kg 280
310

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 750
83
Stiffness to Weight: Axial, points 8.7
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 15 to 20
7.1
Strength to Weight: Bending, points 16 to 18
9.3
Thermal Diffusivity, mm2/s 8.2
110
Thermal Shock Resistance, points 16 to 21
8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Copper (Cu), % 61.7 to 67.8
99.954 to 100
Iron (Fe), % 1.7 to 2.3
0 to 0.0010
Lead (Pb), % 0 to 0.050
0 to 0.00050
Manganese (Mn), % 1.5 to 2.5
0
Nickel (Ni), % 29 to 32
0
Oxygen (O), % 0
0 to 0.040
Selenium (Se), % 0
0 to 0.00020
Silver (Ag), % 0
0 to 0.0025
Sulfur (S), % 0
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020
Zinc (Zn), % 0 to 1.0
0
Residuals, % 0 to 0.5
0