C71640 Copper-nickel vs. C36000 Brass

Both C71640 copper-nickel and C36000 brass are copper alloys. They have 62% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C71640 copper-nickel and the bottom bar is C36000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
100
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 52
39
Tensile Strength: Ultimate (UTS), MPa 490 to 630
330 to 530
Tensile Strength: Yield (Proof), MPa 190 to 460
140 to 260

Thermal Properties

Latent Heat of Fusion, J/g 240
170
Maximum Temperature: Mechanical, °C 260
120
Melting Completion (Liquidus), °C 1180
900
Melting Onset (Solidus), °C 1120
890
Specific Heat Capacity, J/kg-K 410
380
Thermal Conductivity, W/m-K 29
120
Thermal Expansion, µm/m-K 15
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
26
Electrical Conductivity: Equal Weight (Specific), % IACS 7.1
29

Otherwise Unclassified Properties

Base Metal Price, % relative 40
23
Density, g/cm3 8.9
8.2
Embodied Carbon, kg CO2/kg material 5.0
2.6
Embodied Energy, MJ/kg 73
45
Embodied Water, L/kg 280
320

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 750
89 to 340
Stiffness to Weight: Axial, points 8.7
7.0
Stiffness to Weight: Bending, points 20
19
Strength to Weight: Axial, points 15 to 20
11 to 18
Strength to Weight: Bending, points 16 to 18
13 to 18
Thermal Diffusivity, mm2/s 8.2
37
Thermal Shock Resistance, points 16 to 21
11 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 61.7 to 67.8
60 to 63
Iron (Fe), % 1.7 to 2.3
0 to 0.35
Lead (Pb), % 0 to 0.050
2.5 to 3.7
Manganese (Mn), % 1.5 to 2.5
0
Nickel (Ni), % 29 to 32
0
Zinc (Zn), % 0 to 1.0
32.5 to 37.5
Residuals, % 0 to 0.5
0 to 0.5