Both C72150 copper-nickel and C10100 copper are copper alloys. They have 55% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C72150 copper-nickel and the bottom bar is C10100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 150
120
Elongation at Break, % 29
1.5 to 50
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 55
43
Shear Strength, MPa 320
150 to 240
Tensile Strength: Ultimate (UTS), MPa 490
220 to 410
Tensile Strength: Yield (Proof), MPa 210
69 to 400

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Maximum Temperature: Mechanical, °C 600
200
Melting Completion (Liquidus), °C 1210
1080
Melting Onset (Solidus), °C 1250
1080
Specific Heat Capacity, J/kg-K 410
390
Thermal Conductivity, W/m-K 22
390
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.5
100
Electrical Conductivity: Equal Weight (Specific), % IACS 3.6
100

Otherwise Unclassified Properties

Base Metal Price, % relative 45
31
Density, g/cm3 8.9
9.0
Embodied Carbon, kg CO2/kg material 6.1
2.6
Embodied Energy, MJ/kg 88
41
Embodied Water, L/kg 270
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
6.1 to 85
Resilience: Unit (Modulus of Resilience), kJ/m3 150
21 to 690
Stiffness to Weight: Axial, points 9.1
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 15
6.8 to 13
Strength to Weight: Bending, points 15
9.0 to 14
Thermal Diffusivity, mm2/s 6.0
110
Thermal Shock Resistance, points 18
7.8 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 52.5 to 57
99.99 to 100
Iron (Fe), % 0 to 0.1
0
Lead (Pb), % 0 to 0.050
0 to 0.0010
Manganese (Mn), % 0 to 0.050
0
Nickel (Ni), % 43 to 46
0
Oxygen (O), % 0
0 to 0.00050
Phosphorus (P), % 0
0 to 0.00030
Silicon (Si), % 0 to 0.5
0
Zinc (Zn), % 0 to 0.2
0 to 0.00010
Residuals, % 0 to 0.5
0