C72200 Copper-nickel vs. C21000 Brass
Both C72200 copper-nickel and C21000 brass are copper alloys. They have 82% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C72200 copper-nickel and the bottom bar is C21000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 110 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Rockwell B Hardness | 71 to 86 | |
| 36 to 73 |
| Rockwell Superficial 30T Hardness | 64 to 75 | |
| 44 to 68 |
| Shear Modulus, GPa | 48 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 580 | |
| 240 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 190 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1070 |
| Melting Onset (Solidus), °C | 1120 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 34 | |
| 230 |
| Thermal Expansion, µm/m-K | 16 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.5 | |
| 56 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.6 | |
| 57 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 30 |
| Density, g/cm3 | 8.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 2.6 |
| Embodied Energy, MJ/kg | 59 | |
| 42 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.0 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 7.4 to 14 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 9.6 to 15 |
| Thermal Diffusivity, mm2/s | 9.6 | |
| 69 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 8.1 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Chromium (Cr), % | 0.3 to 0.7 | |
| 0 |
| Copper (Cu), % | 78.1 to 84.2 | |
| 94 to 96 |
| Iron (Fe), % | 0.5 to 1.0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 15 to 18 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 3.7 to 6.0 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.2 |