C72700 Copper-nickel vs. SAE-AISI 6150 Steel
C72700 copper-nickel belongs to the copper alloys classification, while SAE-AISI 6150 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C72700 copper-nickel and the bottom bar is SAE-AISI 6150 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 4.0 to 36 | |
| 15 to 23 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 44 | |
| 73 |
| Shear Strength, MPa | 310 to 620 | |
| 400 to 730 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1070 | |
| 630 to 1200 |
| Tensile Strength: Yield (Proof), MPa | 580 to 1060 | |
| 420 to 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 420 |
| Melting Completion (Liquidus), °C | 1100 | |
| 1460 |
| Melting Onset (Solidus), °C | 930 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 54 | |
| 46 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 to 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 2.3 |
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.0 | |
| 2.0 |
| Embodied Energy, MJ/kg | 62 | |
| 28 |
| Embodied Water, L/kg | 350 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 380 | |
| 130 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1420 to 4770 | |
| 460 to 3590 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 14 to 34 | |
| 22 to 43 |
| Strength to Weight: Bending, points | 15 to 26 | |
| 21 to 32 |
| Thermal Diffusivity, mm2/s | 16 | |
| 13 |
| Thermal Shock Resistance, points | 16 to 38 | |
| 20 to 38 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.48 to 0.53 |
| Chromium (Cr), % | 0 | |
| 0.8 to 1.1 |
| Copper (Cu), % | 82.1 to 86 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 96.7 to 97.7 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.3 | |
| 0.7 to 0.9 |
| Nickel (Ni), % | 8.5 to 9.5 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 | |
| 0 to 0.040 |
| Tin (Sn), % | 5.5 to 6.5 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.3 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |