C72900 Copper-nickel vs. CR019A Copper
Both C72900 copper-nickel and CR019A copper are copper alloys. They have 76% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C72900 copper-nickel and the bottom bar is CR019A copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 6.0 to 20 | |
| 15 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1080 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 700 to 920 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 200 |
| Melting Completion (Liquidus), °C | 1120 | |
| 1090 |
| Melting Onset (Solidus), °C | 950 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 29 | |
| 390 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.8 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 35 |
| Density, g/cm3 | 8.8 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 72 | |
| 42 |
| Embodied Water, L/kg | 360 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 to 210 | |
| 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2030 to 3490 | |
| 76 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 27 to 34 | |
| 6.8 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 9.0 |
| Thermal Diffusivity, mm2/s | 8.6 | |
| 110 |
| Thermal Shock Resistance, points | 31 to 38 | |
| 7.8 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Bismuth (Bi), % | 0 | |
| 0 to 0.00050 |
| Copper (Cu), % | 74.1 to 78 | |
| 99.874 to 99.92 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 14.5 to 15.5 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.080 to 0.12 |
| Tin (Sn), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |