C72900 Copper-nickel vs. K94200 Alloy
C72900 copper-nickel belongs to the copper alloys classification, while K94200 alloy belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C72900 copper-nickel and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 140 |
| Elongation at Break, % | 6.0 to 20 | |
| 5.0 to 32 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 54 |
| Shear Strength, MPa | 540 to 630 | |
| 330 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1080 | |
| 500 to 710 |
| Tensile Strength: Yield (Proof), MPa | 700 to 920 | |
| 270 to 650 |
Thermal Properties
| Melting Onset (Solidus), °C | 950 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 500 |
| Thermal Conductivity, W/m-K | 29 | |
| 15 |
| Thermal Expansion, µm/m-K | 17 | |
| 5.0 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.8 | |
| 2.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 3.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 to 210 | |
| 35 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2030 to 3490 | |
| 250 to 1460 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 21 |
| Strength to Weight: Axial, points | 27 to 34 | |
| 17 to 24 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 17 to 22 |
| Thermal Diffusivity, mm2/s | 8.6 | |
| 3.7 |
| Thermal Shock Resistance, points | 31 to 38 | |
| 49 to 70 |