C73100 Nickel Silver vs. 7022 Aluminum
C73100 nickel silver belongs to the copper alloys classification, while 7022 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C73100 nickel silver and the bottom bar is 7022 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 70 |
| Elongation at Break, % | 3.4 to 8.0 | |
| 6.3 to 8.0 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 26 |
| Shear Strength, MPa | 260 to 370 | |
| 290 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 640 | |
| 490 to 540 |
| Tensile Strength: Yield (Proof), MPa | 420 to 590 | |
| 390 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 200 |
| Melting Completion (Liquidus), °C | 1030 | |
| 640 |
| Melting Onset (Solidus), °C | 1000 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 870 |
| Thermal Conductivity, W/m-K | 35 | |
| 140 |
| Thermal Expansion, µm/m-K | 19 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 21 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 65 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 10 |
| Density, g/cm3 | 8.4 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 8.5 |
| Embodied Energy, MJ/kg | 49 | |
| 150 |
| Embodied Water, L/kg | 310 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 35 | |
| 29 to 40 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 790 to 1560 | |
| 1100 to 1500 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 47 |
| Strength to Weight: Axial, points | 15 to 21 | |
| 47 to 51 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 47 to 50 |
| Thermal Diffusivity, mm2/s | 11 | |
| 54 |
| Thermal Shock Resistance, points | 15 to 21 | |
| 21 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 87.9 to 92.4 |
| Chromium (Cr), % | 0 | |
| 0.1 to 0.3 |
| Copper (Cu), % | 70.8 to 78 | |
| 0.5 to 1.0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 2.6 to 3.7 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.1 to 0.4 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 18 to 22 | |
| 4.3 to 5.2 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.15 |