C73100 Nickel Silver vs. C42600 Brass
Both C73100 nickel silver and C42600 brass are copper alloys. They have 83% of their average alloy composition in common.
For each property being compared, the top bar is C73100 nickel silver and the bottom bar is C42600 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 3.4 to 8.0 | |
| 1.1 to 40 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 43 | |
| 42 |
| Shear Strength, MPa | 260 to 370 | |
| 280 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 640 | |
| 410 to 830 |
| Tensile Strength: Yield (Proof), MPa | 420 to 590 | |
| 220 to 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 180 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1030 |
| Melting Onset (Solidus), °C | 1000 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 35 | |
| 110 |
| Thermal Expansion, µm/m-K | 19 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 31 |
| Density, g/cm3 | 8.4 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.9 |
| Embodied Energy, MJ/kg | 49 | |
| 48 |
| Embodied Water, L/kg | 310 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 35 | |
| 9.4 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 790 to 1560 | |
| 230 to 2970 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 15 to 21 | |
| 13 to 27 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 14 to 23 |
| Thermal Diffusivity, mm2/s | 11 | |
| 33 |
| Thermal Shock Resistance, points | 15 to 21 | |
| 15 to 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 70.8 to 78 | |
| 87 to 90 |
| Iron (Fe), % | 0 to 0.1 | |
| 0.050 to 0.2 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 0.050 to 0.2 |
| Phosphorus (P), % | 0 | |
| 0.020 to 0.050 |
| Tin (Sn), % | 0 to 0.1 | |
| 2.5 to 4.0 |
| Zinc (Zn), % | 18 to 22 | |
| 5.3 to 10.4 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.2 |