C73500 Nickel Silver vs. C96700 Copper
Both C73500 nickel silver and C96700 copper are copper alloys. They have 84% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C73500 nickel silver and the bottom bar is C96700 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 140 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 47 | |
| 53 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 580 | |
| 1210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 310 |
| Melting Completion (Liquidus), °C | 1140 | |
| 1170 |
| Melting Onset (Solidus), °C | 1090 | |
| 1110 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 400 |
| Thermal Conductivity, W/m-K | 36 | |
| 30 |
| Thermal Expansion, µm/m-K | 17 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 90 |
| Density, g/cm3 | 8.7 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 4.0 | |
| 9.5 |
| Embodied Energy, MJ/kg | 61 | |
| 140 |
| Embodied Water, L/kg | 300 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.0 | |
| 8.9 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 38 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 29 |
| Thermal Diffusivity, mm2/s | 10 | |
| 8.5 |
| Thermal Shock Resistance, points | 13 to 19 | |
| 40 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Beryllium (Be), % | 0 | |
| 1.1 to 1.2 |
| Copper (Cu), % | 70.5 to 73.5 | |
| 62.4 to 68.8 |
| Iron (Fe), % | 0 to 0.25 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.4 to 1.0 |
| Nickel (Ni), % | 16.5 to 19.5 | |
| 29 to 33 |
| Silicon (Si), % | 0 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.35 |
| Zinc (Zn), % | 5.7 to 13 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.15 to 0.35 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |