C74400 Nickel Silver vs. C66100 Bronze

Both C74400 nickel silver and C66100 bronze are copper alloys. They have 65% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C74400 nickel silver and the bottom bar is C66100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Elongation at Break, % 43
8.0 to 40
Poisson's Ratio 0.31
0.34
Shear Modulus, GPa 39
43
Shear Strength, MPa 240
280 to 460
Tensile Strength: Ultimate (UTS), MPa 350
410 to 790
Tensile Strength: Yield (Proof), MPa 120
120 to 430

Thermal Properties

Latent Heat of Fusion, J/g 180
260
Maximum Temperature: Mechanical, °C 140
200
Melting Completion (Liquidus), °C 930
1050
Melting Onset (Solidus), °C 910
1000
Specific Heat Capacity, J/kg-K 390
400
Thermal Conductivity, W/m-K 120
34
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Base Metal Price, % relative 25
29
Density, g/cm3 8.2
8.7
Embodied Carbon, kg CO2/kg material 2.9
2.6
Embodied Energy, MJ/kg 48
42
Embodied Water, L/kg 320
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
53 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 63
60 to 790
Stiffness to Weight: Axial, points 7.4
7.4
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 12
13 to 25
Strength to Weight: Bending, points 14
14 to 22
Thermal Diffusivity, mm2/s 37
9.7
Thermal Shock Resistance, points 12
15 to 29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 62 to 66
92 to 97
Iron (Fe), % 0 to 0.050
0 to 0.25
Lead (Pb), % 0 to 0.050
0.2 to 0.8
Manganese (Mn), % 0
0 to 1.5
Nickel (Ni), % 2.0 to 4.0
0
Silicon (Si), % 0
2.8 to 3.5
Zinc (Zn), % 29.6 to 36
0 to 1.5
Residuals, % 0 to 0.3
0 to 0.5