C74500 Nickel Silver vs. C41300 Brass
Both C74500 nickel silver and C41300 brass are copper alloys. They have 73% of their average alloy composition in common.
For each property being compared, the top bar is C74500 nickel silver and the bottom bar is C41300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 3.0 to 24 | |
| 2.0 to 44 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Rockwell B Hardness | 66 to 94 | |
| 53 to 88 |
| Rockwell Superficial 30T Hardness | 60 to 79 | |
| 20 to 77 |
| Shear Modulus, GPa | 44 | |
| 42 |
| Shear Strength, MPa | 310 to 380 | |
| 230 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 700 | |
| 300 to 630 |
| Tensile Strength: Yield (Proof), MPa | 380 to 600 | |
| 120 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 180 |
| Melting Completion (Liquidus), °C | 1020 | |
| 1040 |
| Melting Onset (Solidus), °C | 970 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 45 | |
| 130 |
| Thermal Expansion, µm/m-K | 19 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.7 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 29 |
| Density, g/cm3 | 8.3 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 54 | |
| 44 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 160 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 to 1540 | |
| 69 to 1440 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 13 to 23 | |
| 9.6 to 20 |
| Strength to Weight: Bending, points | 14 to 21 | |
| 11 to 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 40 |
| Thermal Shock Resistance, points | 13 to 23 | |
| 11 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 63.5 to 66.5 | |
| 89 to 93 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.7 to 1.3 |
| Zinc (Zn), % | 21.2 to 27.5 | |
| 5.1 to 10.3 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |