C74500 Nickel Silver vs. C93800 Bronze

Both C74500 nickel silver and C93800 bronze are copper alloys. They have 66% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C74500 nickel silver and the bottom bar is C93800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
96
Elongation at Break, % 3.0 to 24
9.7
Poisson's Ratio 0.32
0.35
Shear Modulus, GPa 44
35
Tensile Strength: Ultimate (UTS), MPa 390 to 700
200
Tensile Strength: Yield (Proof), MPa 380 to 600
120

Thermal Properties

Latent Heat of Fusion, J/g 190
170
Maximum Temperature: Mechanical, °C 170
140
Melting Completion (Liquidus), °C 1020
940
Melting Onset (Solidus), °C 970
850
Specific Heat Capacity, J/kg-K 390
340
Thermal Conductivity, W/m-K 45
52
Thermal Expansion, µm/m-K 19
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.0
11
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
11

Otherwise Unclassified Properties

Base Metal Price, % relative 29
31
Density, g/cm3 8.3
9.1
Embodied Carbon, kg CO2/kg material 3.4
3.2
Embodied Energy, MJ/kg 54
51
Embodied Water, L/kg 310
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12 to 160
17
Resilience: Unit (Modulus of Resilience), kJ/m3 620 to 1540
70
Stiffness to Weight: Axial, points 7.7
5.9
Stiffness to Weight: Bending, points 19
17
Strength to Weight: Axial, points 13 to 23
6.1
Strength to Weight: Bending, points 14 to 21
8.4
Thermal Diffusivity, mm2/s 14
17
Thermal Shock Resistance, points 13 to 23
8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.8
Copper (Cu), % 63.5 to 66.5
75 to 79
Iron (Fe), % 0 to 0.25
0 to 0.15
Lead (Pb), % 0 to 0.1
13 to 16
Manganese (Mn), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
0 to 1.0
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 0
6.3 to 7.5
Zinc (Zn), % 21.2 to 27.5
0 to 0.8
Residuals, % 0 to 0.5
0 to 1.0