C75200 Nickel Silver vs. ASTM B563 Pd-Ag-Cu

C75200 nickel silver belongs to the copper alloys classification, while ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C75200 nickel silver and the bottom bar is ASTM B563 Pd-Ag-Cu.

UNS C75200 (CW409J) Nickel Silver ASTM B563 Palladium-Silver-Copper Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		100

Poisson's Ratio		0.32
Poisson's Ratio		0.37

Shear Modulus, GPa		47
Shear Modulus, GPa		37

Tensile Strength: Ultimate (UTS), MPa		400 to 660
Tensile Strength: Ultimate (UTS), MPa		760 to 1170

Thermal Properties

Latent Heat of Fusion, J/g		210
Latent Heat of Fusion, J/g		150

Melting Completion (Liquidus), °C		1110
Melting Completion (Liquidus), °C		1180

Melting Onset (Solidus), °C		1070
Melting Onset (Solidus), °C		1030

Specific Heat Capacity, J/kg-K		400
Specific Heat Capacity, J/kg-K		260

Thermal Expansion, µm/m-K		18
Thermal Expansion, µm/m-K		14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		6.0
Electrical Conductivity: Equal Volume, % IACS		5.6 to 6.7

Electrical Conductivity: Equal Weight (Specific), % IACS		6.3
Electrical Conductivity: Equal Weight (Specific), % IACS		4.6 to 5.5

Otherwise Unclassified Properties

Density, g/cm³		8.5
Density, g/cm³		11

Common Calculations

Stiffness to Weight: Axial, points		8.0
Stiffness to Weight: Axial, points		5.2

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		14

Strength to Weight: Axial, points		13 to 21
Strength to Weight: Axial, points		19 to 30

Strength to Weight: Bending, points		14 to 20
Strength to Weight: Bending, points		17 to 22

Thermal Shock Resistance, points		13 to 22
Thermal Shock Resistance, points		39 to 61

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452

Copper (Cu), %		63.5 to 66.5
Copper (Cu), %		15.5 to 16.5

Iron (Fe), %		0 to 0.25
Iron (Fe), %		0

Lead (Pb), %		0 to 0.050
Lead (Pb), %		0

Manganese (Mn), %		0 to 0.5
Manganese (Mn), %		0

Nickel (Ni), %		16.5 to 19.5
Nickel (Ni), %		0.8 to 1.2

Palladium (Pd), %		0
Palladium (Pd), %		43 to 45

Platinum (Pt), %		0
Platinum (Pt), %		0.8 to 1.2

Silver (Ag), %		0
Silver (Ag), %		37 to 39

Zinc (Zn), %		12.7 to 20
Zinc (Zn), %		0

Residuals, %		0 to 0.5
Residuals, %		0 to 0.4