C75700 Nickel Silver vs. 4104 Aluminum
C75700 nickel silver belongs to the copper alloys classification, while 4104 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C75700 nickel silver and the bottom bar is 4104 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 71 |
| Elongation at Break, % | 3.2 to 22 | |
| 2.4 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 45 | |
| 27 |
| Shear Strength, MPa | 350 to 370 | |
| 63 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 610 | |
| 110 |
| Tensile Strength: Yield (Proof), MPa | 470 to 580 | |
| 60 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 540 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 160 |
| Melting Completion (Liquidus), °C | 1040 | |
| 600 |
| Melting Onset (Solidus), °C | 990 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 900 |
| Thermal Conductivity, W/m-K | 40 | |
| 130 |
| Thermal Expansion, µm/m-K | 16 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 9.5 |
| Density, g/cm3 | 8.4 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 8.0 |
| Embodied Energy, MJ/kg | 56 | |
| 150 |
| Embodied Water, L/kg | 310 | |
| 1080 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 120 | |
| 2.3 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 930 to 1410 | |
| 25 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 15 |
| Stiffness to Weight: Bending, points | 19 | |
| 54 |
| Strength to Weight: Axial, points | 19 to 20 | |
| 12 |
| Strength to Weight: Bending, points | 19 | |
| 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 58 |
| Thermal Shock Resistance, points | 22 to 23 | |
| 5.1 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 85.8 to 90 |
| Bismuth (Bi), % | 0 | |
| 0.020 to 0.2 |
| Copper (Cu), % | 63.5 to 66.5 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.8 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 1.0 to 2.0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 11 to 13 | |
| 0 |
| Silicon (Si), % | 0 | |
| 9.0 to 10.5 |
| Zinc (Zn), % | 19.2 to 25.5 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.15 |