C75700 Nickel Silver vs. B535.0 Aluminum

C75700 nickel silver belongs to the copper alloys classification, while B535.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is B535.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
66
Elongation at Break, % 3.2 to 22
10
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 45
25
Shear Strength, MPa 350 to 370
210
Tensile Strength: Ultimate (UTS), MPa 590 to 610
260
Tensile Strength: Yield (Proof), MPa 470 to 580
130

Thermal Properties

Latent Heat of Fusion, J/g 200
390
Maximum Temperature: Mechanical, °C 180
170
Melting Completion (Liquidus), °C 1040
630
Melting Onset (Solidus), °C 990
550
Specific Heat Capacity, J/kg-K 390
910
Thermal Conductivity, W/m-K 40
96
Thermal Expansion, µm/m-K 16
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
24
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
82

Otherwise Unclassified Properties

Base Metal Price, % relative 30
9.5
Density, g/cm3 8.4
2.6
Embodied Carbon, kg CO2/kg material 3.6
9.4
Embodied Energy, MJ/kg 56
160
Embodied Water, L/kg 310
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 120
22
Resilience: Unit (Modulus of Resilience), kJ/m3 930 to 1410
130
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 19
51
Strength to Weight: Axial, points 19 to 20
28
Strength to Weight: Bending, points 19
35
Thermal Diffusivity, mm2/s 12
40
Thermal Shock Resistance, points 22 to 23
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
91.7 to 93.4
Copper (Cu), % 63.5 to 66.5
0 to 0.1
Iron (Fe), % 0 to 0.25
0 to 0.15
Lead (Pb), % 0 to 0.050
0
Magnesium (Mg), % 0
6.5 to 7.5
Manganese (Mn), % 0 to 0.5
0 to 0.050
Nickel (Ni), % 11 to 13
0
Silicon (Si), % 0
0 to 0.15
Titanium (Ti), % 0
0.1 to 0.25
Zinc (Zn), % 19.2 to 25.5
0
Residuals, % 0 to 0.5
0 to 0.15