C75700 Nickel Silver vs. CC334G Bronze

Both C75700 nickel silver and CC334G bronze are copper alloys. They have 71% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is CC334G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 3.2 to 22
5.6
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 45
45
Tensile Strength: Ultimate (UTS), MPa 590 to 610
810
Tensile Strength: Yield (Proof), MPa 470 to 580
410

Thermal Properties

Latent Heat of Fusion, J/g 200
240
Maximum Temperature: Mechanical, °C 180
240
Melting Completion (Liquidus), °C 1040
1080
Melting Onset (Solidus), °C 990
1020
Specific Heat Capacity, J/kg-K 390
450
Thermal Conductivity, W/m-K 40
41
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 30
29
Density, g/cm3 8.4
8.2
Embodied Carbon, kg CO2/kg material 3.6
3.6
Embodied Energy, MJ/kg 56
59
Embodied Water, L/kg 310
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 120
38
Resilience: Unit (Modulus of Resilience), kJ/m3 930 to 1410
710
Stiffness to Weight: Axial, points 7.8
8.1
Stiffness to Weight: Bending, points 19
20
Strength to Weight: Axial, points 19 to 20
28
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 22 to 23
28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
10 to 12
Copper (Cu), % 63.5 to 66.5
72 to 84.5
Iron (Fe), % 0 to 0.25
3.0 to 7.0
Lead (Pb), % 0 to 0.050
0 to 0.050
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0 to 0.5
0 to 2.5
Nickel (Ni), % 11 to 13
4.0 to 7.5
Silicon (Si), % 0
0 to 0.1
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 19.2 to 25.5
0 to 0.5
Residuals, % 0 to 0.5
0