C75700 Nickel Silver vs. Type 2 Pewter

C75700 nickel silver belongs to the copper alloys classification, while Type 2 pewter belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is Type 2 pewter.

UNS C75700 (CW403J) Nickel Silver Type 2 (L13912) Sheet Pewter

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		52

Poisson's Ratio		0.32
Poisson's Ratio		0.35

Shear Modulus, GPa		45
Shear Modulus, GPa		19

Tensile Strength: Ultimate (UTS), MPa		590 to 610
Tensile Strength: Ultimate (UTS), MPa		52 to 68

Thermal Properties

Latent Heat of Fusion, J/g		200
Latent Heat of Fusion, J/g		69

Melting Completion (Liquidus), °C		1040
Melting Completion (Liquidus), °C		300

Melting Onset (Solidus), °C		990
Melting Onset (Solidus), °C		240

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		220

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		21

Otherwise Unclassified Properties

Base Metal Price, % relative		30
Base Metal Price, % relative		75

Density, g/cm³		8.4
Density, g/cm³		7.3

Embodied Carbon, kg CO₂/kg material		3.6
Embodied Carbon, kg CO₂/kg material		12

Embodied Energy, MJ/kg		56
Embodied Energy, MJ/kg		210

Embodied Water, L/kg		310
Embodied Water, L/kg		1220

Common Calculations

Stiffness to Weight: Axial, points		7.8
Stiffness to Weight: Axial, points		3.9

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		17

Strength to Weight: Axial, points		19 to 20
Strength to Weight: Axial, points		2.0 to 2.6

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		4.3 to 5.1

Thermal Shock Resistance, points		22 to 23
Thermal Shock Resistance, points		3.4 to 4.4

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452

Antimony (Sb), %		0
Antimony (Sb), %		5.0 to 7.5

Arsenic (As), %		0
Arsenic (As), %		0 to 0.050

Copper (Cu), %		63.5 to 66.5
Copper (Cu), %		1.5 to 3.0

Iron (Fe), %		0 to 0.25
Iron (Fe), %		0 to 0.015

Lead (Pb), %		0 to 0.050
Lead (Pb), %		0 to 0.050

Manganese (Mn), %		0 to 0.5
Manganese (Mn), %		0

Nickel (Ni), %		11 to 13
Nickel (Ni), %		0

Tin (Sn), %		0
Tin (Sn), %		90 to 93

Zinc (Zn), %		19.2 to 25.5
Zinc (Zn), %		0 to 0.0050

Residuals, %		0 to 0.5
Residuals, %		0