C75700 Nickel Silver vs. C26800 Brass

Both C75700 nickel silver and C26800 brass are copper alloys. They have 88% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is C26800 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Poisson's Ratio 0.32
0.31
Shear Modulus, GPa 45
40
Tensile Strength: Ultimate (UTS), MPa 590 to 610
310 to 650

Thermal Properties

Latent Heat of Fusion, J/g 200
180
Maximum Temperature: Mechanical, °C 180
130
Melting Completion (Liquidus), °C 1040
930
Melting Onset (Solidus), °C 990
900
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 40
120
Thermal Expansion, µm/m-K 16
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
30

Otherwise Unclassified Properties

Base Metal Price, % relative 30
24
Density, g/cm3 8.4
8.1
Embodied Carbon, kg CO2/kg material 3.6
2.7
Embodied Energy, MJ/kg 56
45
Embodied Water, L/kg 310
320

Common Calculations

Stiffness to Weight: Axial, points 7.8
7.2
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 19 to 20
11 to 22
Strength to Weight: Bending, points 19
13 to 21
Thermal Diffusivity, mm2/s 12
37
Thermal Shock Resistance, points 22 to 23
10 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 63.5 to 66.5
64 to 68.5
Iron (Fe), % 0 to 0.25
0 to 0.050
Lead (Pb), % 0 to 0.050
0 to 0.15
Manganese (Mn), % 0 to 0.5
0
Nickel (Ni), % 11 to 13
0
Zinc (Zn), % 19.2 to 25.5
31 to 36
Residuals, % 0 to 0.5
0 to 0.3

Comparable Variants