C75700 Nickel Silver vs. C77400 Nickel Silver

Both C75700 nickel silver and C77400 nickel silver are copper alloys. They have 78% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is C77400 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 3.2 to 22
25
Poisson's Ratio 0.32
0.3
Shear Modulus, GPa 45
42
Shear Strength, MPa 350 to 370
360
Tensile Strength: Ultimate (UTS), MPa 590 to 610
570
Tensile Strength: Yield (Proof), MPa 470 to 580
250

Thermal Properties

Latent Heat of Fusion, J/g 200
170
Maximum Temperature: Mechanical, °C 180
130
Melting Completion (Liquidus), °C 1040
810
Melting Onset (Solidus), °C 990
770
Specific Heat Capacity, J/kg-K 390
390
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
31

Otherwise Unclassified Properties

Base Metal Price, % relative 30
25
Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 3.6
3.5
Embodied Energy, MJ/kg 56
57
Embodied Water, L/kg 310
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 120
120
Resilience: Unit (Modulus of Resilience), kJ/m3 930 to 1410
290
Stiffness to Weight: Axial, points 7.8
7.7
Stiffness to Weight: Bending, points 19
20
Strength to Weight: Axial, points 19 to 20
20
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 22 to 23
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 63.5 to 66.5
43 to 47
Iron (Fe), % 0 to 0.25
0
Lead (Pb), % 0 to 0.050
0 to 0.2
Manganese (Mn), % 0 to 0.5
0
Nickel (Ni), % 11 to 13
9.0 to 11
Zinc (Zn), % 19.2 to 25.5
41.3 to 48
Residuals, % 0 to 0.5
0 to 0.5