C75700 Nickel Silver vs. C84000 Brass

Both C75700 nickel silver and C84000 brass are copper alloys. They have 76% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is C84000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 3.2 to 22
27
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 45
42
Tensile Strength: Ultimate (UTS), MPa 590 to 610
250
Tensile Strength: Yield (Proof), MPa 470 to 580
140

Thermal Properties

Latent Heat of Fusion, J/g 200
190
Maximum Temperature: Mechanical, °C 180
170
Melting Completion (Liquidus), °C 1040
1040
Melting Onset (Solidus), °C 990
940
Specific Heat Capacity, J/kg-K 390
380
Thermal Conductivity, W/m-K 40
72
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
16
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
17

Otherwise Unclassified Properties

Base Metal Price, % relative 30
30
Density, g/cm3 8.4
8.6
Embodied Carbon, kg CO2/kg material 3.6
3.0
Embodied Energy, MJ/kg 56
49
Embodied Water, L/kg 310
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 120
58
Resilience: Unit (Modulus of Resilience), kJ/m3 930 to 1410
83
Stiffness to Weight: Axial, points 7.8
7.2
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 19 to 20
8.2
Strength to Weight: Bending, points 19
10
Thermal Diffusivity, mm2/s 12
22
Thermal Shock Resistance, points 22 to 23
9.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.020
Boron (B), % 0
0 to 0.1
Copper (Cu), % 63.5 to 66.5
82 to 89
Iron (Fe), % 0 to 0.25
0 to 0.4
Lead (Pb), % 0 to 0.050
0 to 0.090
Manganese (Mn), % 0 to 0.5
0 to 0.010
Nickel (Ni), % 11 to 13
0.5 to 2.0
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0
0 to 0.0050
Sulfur (S), % 0
0.1 to 0.65
Tin (Sn), % 0
2.0 to 4.0
Zinc (Zn), % 19.2 to 25.5
5.0 to 14
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0 to 0.5
0 to 0.7