C75700 Nickel Silver vs. C84100 Brass

Both C75700 nickel silver and C84100 brass are copper alloys. They have 82% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is C84100 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 3.2 to 22
13
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 45
39
Tensile Strength: Ultimate (UTS), MPa 590 to 610
230
Tensile Strength: Yield (Proof), MPa 470 to 580
81

Thermal Properties

Latent Heat of Fusion, J/g 200
190
Maximum Temperature: Mechanical, °C 180
160
Melting Completion (Liquidus), °C 1040
1000
Melting Onset (Solidus), °C 990
810
Specific Heat Capacity, J/kg-K 390
380
Thermal Conductivity, W/m-K 40
110
Thermal Expansion, µm/m-K 16
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
23
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
25

Otherwise Unclassified Properties

Base Metal Price, % relative 30
29
Density, g/cm3 8.4
8.5
Embodied Carbon, kg CO2/kg material 3.6
2.9
Embodied Energy, MJ/kg 56
48
Embodied Water, L/kg 310
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 120
24
Resilience: Unit (Modulus of Resilience), kJ/m3 930 to 1410
30
Stiffness to Weight: Axial, points 7.8
7.1
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 19 to 20
7.4
Strength to Weight: Bending, points 19
9.7
Thermal Diffusivity, mm2/s 12
33
Thermal Shock Resistance, points 22 to 23
7.8

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.050
Bismuth (Bi), % 0
0 to 0.090
Copper (Cu), % 63.5 to 66.5
78 to 85
Iron (Fe), % 0 to 0.25
0 to 0.3
Lead (Pb), % 0 to 0.050
0.050 to 0.25
Manganese (Mn), % 0 to 0.5
0
Nickel (Ni), % 11 to 13
0 to 0.5
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0
0 to 0.010
Tin (Sn), % 0
1.5 to 4.5
Zinc (Zn), % 19.2 to 25.5
12 to 20
Residuals, % 0 to 0.5
0 to 0.5