C75700 Nickel Silver vs. C95410 Bronze

Both C75700 nickel silver and C95410 bronze are copper alloys. They have 68% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C75700 nickel silver and the bottom bar is C95410 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 3.2 to 22
9.1 to 13
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 45
43
Tensile Strength: Ultimate (UTS), MPa 590 to 610
620 to 740
Tensile Strength: Yield (Proof), MPa 470 to 580
260 to 380

Thermal Properties

Latent Heat of Fusion, J/g 200
230
Maximum Temperature: Mechanical, °C 180
230
Melting Completion (Liquidus), °C 1040
1040
Melting Onset (Solidus), °C 990
1030
Specific Heat Capacity, J/kg-K 390
440
Thermal Conductivity, W/m-K 40
59
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
13
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
14

Otherwise Unclassified Properties

Base Metal Price, % relative 30
28
Density, g/cm3 8.4
8.2
Embodied Carbon, kg CO2/kg material 3.6
3.3
Embodied Energy, MJ/kg 56
54
Embodied Water, L/kg 310
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 120
57 to 64
Resilience: Unit (Modulus of Resilience), kJ/m3 930 to 1410
280 to 630
Stiffness to Weight: Axial, points 7.8
7.8
Stiffness to Weight: Bending, points 19
20
Strength to Weight: Axial, points 19 to 20
21 to 25
Strength to Weight: Bending, points 19
20 to 22
Thermal Diffusivity, mm2/s 12
16
Thermal Shock Resistance, points 22 to 23
22 to 26

Alloy Composition

Aluminum (Al), % 0
10 to 11.5
Copper (Cu), % 63.5 to 66.5
83 to 85.5
Iron (Fe), % 0 to 0.25
3.0 to 5.0
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0 to 0.5
0 to 0.5
Nickel (Ni), % 11 to 13
1.5 to 2.5
Zinc (Zn), % 19.2 to 25.5
0
Residuals, % 0 to 0.5
0 to 0.5