C76200 Nickel Silver vs. Chromium 33
C76200 nickel silver belongs to the copper alloys classification, while chromium 33 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is C76200 nickel silver and the bottom bar is chromium 33.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Poisson's Ratio | 0.31 | |
| 0.27 |
| Shear Modulus, GPa | 44 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 790 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 320 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Expansion, µm/m-K | 19 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 36 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 6.0 |
| Embodied Energy, MJ/kg | 57 | |
| 84 |
| Embodied Water, L/kg | 310 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 13 to 27 | |
| 30 |
| Strength to Weight: Bending, points | 14 to 23 | |
| 25 |
| Thermal Shock Resistance, points | 13 to 26 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.015 |
| Chromium (Cr), % | 0 | |
| 31 to 35 |
| Copper (Cu), % | 57 to 61 | |
| 0.3 to 1.2 |
| Iron (Fe), % | 0 to 0.25 | |
| 25.7 to 37.9 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0.5 to 2.0 |
| Nickel (Ni), % | 11 to 13.5 | |
| 30 to 33 |
| Nitrogen (N), % | 0 | |
| 0.35 to 0.6 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 24.2 to 32 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |