C76200 Nickel Silver vs. Nickel 890
C76200 nickel silver belongs to the copper alloys classification, while nickel 890 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C76200 nickel silver and the bottom bar is nickel 890.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 44 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 790 | |
| 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1390 |
| Melting Onset (Solidus), °C | 980 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Expansion, µm/m-K | 19 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 47 |
| Density, g/cm3 | 8.2 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 8.2 |
| Embodied Energy, MJ/kg | 57 | |
| 120 |
| Embodied Water, L/kg | 310 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 27 | |
| 20 |
| Strength to Weight: Bending, points | 14 to 23 | |
| 19 |
| Thermal Shock Resistance, points | 13 to 26 | |
| 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.050 to 0.6 |
| Carbon (C), % | 0 | |
| 0.060 to 0.14 |
| Chromium (Cr), % | 0 | |
| 23.5 to 28.5 |
| Copper (Cu), % | 57 to 61 | |
| 0 to 0.75 |
| Iron (Fe), % | 0 to 0.25 | |
| 17.3 to 33.9 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 11 to 13.5 | |
| 40 to 45 |
| Niobium (Nb), % | 0 | |
| 0.2 to 1.0 |
| Silicon (Si), % | 0 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tantalum (Ta), % | 0 | |
| 0.1 to 0.6 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.6 |
| Zinc (Zn), % | 24.2 to 32 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |