C78200 Nickel Silver vs. 2618 Aluminum
C78200 nickel silver belongs to the copper alloys classification, while 2618 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C78200 nickel silver and the bottom bar is 2618 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 71 |
| Elongation at Break, % | 3.0 to 40 | |
| 5.8 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 43 | |
| 27 |
| Shear Strength, MPa | 280 to 400 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 420 |
| Tensile Strength: Yield (Proof), MPa | 170 to 570 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 210 |
| Melting Completion (Liquidus), °C | 1000 | |
| 640 |
| Melting Onset (Solidus), °C | 970 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 880 |
| Thermal Conductivity, W/m-K | 48 | |
| 160 |
| Thermal Expansion, µm/m-K | 19 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 37 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 11 |
| Density, g/cm3 | 8.4 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 52 | |
| 150 |
| Embodied Water, L/kg | 310 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 120 | |
| 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1440 | |
| 850 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 47 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 40 |
| Strength to Weight: Bending, points | 14 to 19 | |
| 42 |
| Thermal Diffusivity, mm2/s | 15 | |
| 62 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 92.4 to 94.9 |
| Copper (Cu), % | 63 to 67 | |
| 1.9 to 2.7 |
| Iron (Fe), % | 0 to 0.35 | |
| 0.9 to 1.3 |
| Lead (Pb), % | 1.5 to 2.5 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 1.3 to 1.8 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 7.0 to 9.0 | |
| 0.9 to 1.2 |
| Silicon (Si), % | 0 | |
| 0.1 to 0.25 |
| Titanium (Ti), % | 0 | |
| 0.040 to 0.1 |
| Zinc (Zn), % | 20.2 to 28.5 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.15 |