C78200 Nickel Silver vs. EN 1.8550 Steel
C78200 nickel silver belongs to the copper alloys classification, while EN 1.8550 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C78200 nickel silver and the bottom bar is EN 1.8550 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 3.0 to 40 | |
| 11 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 73 |
| Shear Strength, MPa | 280 to 400 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 1000 |
| Tensile Strength: Yield (Proof), MPa | 170 to 570 | |
| 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 440 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1450 |
| Melting Onset (Solidus), °C | 970 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 48 | |
| 40 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 3.4 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 1.7 |
| Embodied Energy, MJ/kg | 52 | |
| 23 |
| Embodied Water, L/kg | 310 | |
| 67 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 120 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1440 | |
| 1550 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 36 |
| Strength to Weight: Bending, points | 14 to 19 | |
| 29 |
| Thermal Diffusivity, mm2/s | 15 | |
| 11 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.8 to 1.2 |
| Carbon (C), % | 0 | |
| 0.3 to 0.37 |
| Chromium (Cr), % | 0 | |
| 1.5 to 1.8 |
| Copper (Cu), % | 63 to 67 | |
| 0 |
| Iron (Fe), % | 0 to 0.35 | |
| 94.4 to 96.3 |
| Lead (Pb), % | 1.5 to 2.5 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 7.0 to 9.0 | |
| 0.85 to 1.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Zinc (Zn), % | 20.2 to 28.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |