C79200 Nickel Silver vs. Nickel 908
C79200 nickel silver belongs to the copper alloys classification, while nickel 908 belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C79200 nickel silver and the bottom bar is nickel 908.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 180 |
| Poisson's Ratio | 0.32 | |
| 0.3 |
| Shear Modulus, GPa | 44 | |
| 70 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 540 | |
| 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 920 |
| Melting Completion (Liquidus), °C | 950 | |
| 1430 |
| Melting Onset (Solidus), °C | 910 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 460 |
| Thermal Conductivity, W/m-K | 42 | |
| 11 |
| Thermal Expansion, µm/m-K | 19 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 50 |
| Density, g/cm3 | 8.4 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 9.3 |
| Embodied Energy, MJ/kg | 56 | |
| 140 |
| Embodied Water, L/kg | 310 | |
| 170 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 12 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 18 | |
| 45 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 33 |
| Thermal Diffusivity, mm2/s | 13 | |
| 2.9 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 61 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.75 to 1.3 |
| Boron (B), % | 0 | |
| 0 to 0.012 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 3.8 to 4.5 |
| Cobalt (Co), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 59 to 66.5 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 35.6 to 44.6 |
| Lead (Pb), % | 0.8 to 1.4 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.0 |
| Nickel (Ni), % | 11 to 13 | |
| 47 to 51 |
| Niobium (Nb), % | 0 | |
| 2.7 to 3.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 0 | |
| 1.2 to 1.8 |
| Zinc (Zn), % | 17.9 to 29.2 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |