C79600 Nickel Silver vs. 3005 Aluminum

C79600 nickel silver belongs to the copper alloys classification, while 3005 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is 3005 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
70
Elongation at Break, % 15
1.1 to 16
Poisson's Ratio 0.3
0.33
Shear Modulus, GPa 43
26
Shear Strength, MPa 290
84 to 150
Tensile Strength: Ultimate (UTS), MPa 480
140 to 270
Tensile Strength: Yield (Proof), MPa 300
51 to 240

Thermal Properties

Latent Heat of Fusion, J/g 180
400
Maximum Temperature: Mechanical, °C 130
180
Melting Completion (Liquidus), °C 930
660
Melting Onset (Solidus), °C 880
640
Specific Heat Capacity, J/kg-K 390
900
Thermal Conductivity, W/m-K 36
160
Thermal Expansion, µm/m-K 21
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
42
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
140

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.5
Density, g/cm3 7.9
2.8
Embodied Carbon, kg CO2/kg material 3.5
8.2
Embodied Energy, MJ/kg 57
150
Embodied Water, L/kg 310
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
2.2 to 18
Resilience: Unit (Modulus of Resilience), kJ/m3 400
18 to 390
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
49
Strength to Weight: Axial, points 17
14 to 27
Strength to Weight: Bending, points 17
21 to 33
Thermal Diffusivity, mm2/s 12
64
Thermal Shock Resistance, points 15
6.0 to 12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
95.7 to 98.8
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 43.5 to 46.5
0 to 0.3
Iron (Fe), % 0
0 to 0.7
Lead (Pb), % 0.8 to 1.2
0
Magnesium (Mg), % 0
0.2 to 0.6
Manganese (Mn), % 1.5 to 2.5
1.0 to 1.5
Nickel (Ni), % 9.0 to 11
0
Silicon (Si), % 0
0 to 0.6
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 38.3 to 45.2
0 to 0.25
Residuals, % 0 to 0.5
0 to 0.15