C79600 Nickel Silver vs. 6081 Aluminum

C79600 nickel silver belongs to the copper alloys classification, while 6081 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is 6081 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
69
Elongation at Break, % 15
9.0
Poisson's Ratio 0.3
0.33
Shear Modulus, GPa 43
26
Shear Strength, MPa 290
180
Tensile Strength: Ultimate (UTS), MPa 480
310
Tensile Strength: Yield (Proof), MPa 300
270

Thermal Properties

Latent Heat of Fusion, J/g 180
410
Maximum Temperature: Mechanical, °C 130
160
Melting Completion (Liquidus), °C 930
640
Melting Onset (Solidus), °C 880
610
Specific Heat Capacity, J/kg-K 390
900
Thermal Conductivity, W/m-K 36
180
Thermal Expansion, µm/m-K 21
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
47
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
160

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.5
Density, g/cm3 7.9
2.7
Embodied Carbon, kg CO2/kg material 3.5
8.3
Embodied Energy, MJ/kg 57
150
Embodied Water, L/kg 310
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
27
Resilience: Unit (Modulus of Resilience), kJ/m3 400
540
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
50
Strength to Weight: Axial, points 17
32
Strength to Weight: Bending, points 17
37
Thermal Diffusivity, mm2/s 12
74
Thermal Shock Resistance, points 15
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
96.3 to 98.6
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 43.5 to 46.5
0 to 0.1
Iron (Fe), % 0
0 to 0.5
Lead (Pb), % 0.8 to 1.2
0
Magnesium (Mg), % 0
0.6 to 1.0
Manganese (Mn), % 1.5 to 2.5
0.1 to 0.45
Nickel (Ni), % 9.0 to 11
0
Silicon (Si), % 0
0.7 to 1.1
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 38.3 to 45.2
0 to 0.2
Residuals, % 0 to 0.5
0 to 0.15