C79600 Nickel Silver vs. 710.0 Aluminum

C79600 nickel silver belongs to the copper alloys classification, while 710.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is 710.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
70
Elongation at Break, % 15
2.2 to 3.6
Poisson's Ratio 0.3
0.32
Shear Modulus, GPa 43
26
Shear Strength, MPa 290
180
Tensile Strength: Ultimate (UTS), MPa 480
240 to 250
Tensile Strength: Yield (Proof), MPa 300
160

Thermal Properties

Latent Heat of Fusion, J/g 180
380
Maximum Temperature: Mechanical, °C 130
170
Melting Completion (Liquidus), °C 930
650
Melting Onset (Solidus), °C 880
610
Specific Heat Capacity, J/kg-K 390
870
Thermal Conductivity, W/m-K 36
140
Thermal Expansion, µm/m-K 21
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
35
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
110

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.5
Density, g/cm3 7.9
3.0
Embodied Carbon, kg CO2/kg material 3.5
8.0
Embodied Energy, MJ/kg 57
150
Embodied Water, L/kg 310
1130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
4.9 to 7.9
Resilience: Unit (Modulus of Resilience), kJ/m3 400
180 to 190
Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
46
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 17
29
Thermal Diffusivity, mm2/s 12
53
Thermal Shock Resistance, points 15
10 to 11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
90.5 to 93.1
Copper (Cu), % 43.5 to 46.5
0.35 to 0.65
Iron (Fe), % 0
0 to 0.5
Lead (Pb), % 0.8 to 1.2
0
Magnesium (Mg), % 0
0.6 to 0.8
Manganese (Mn), % 1.5 to 2.5
0 to 0.050
Nickel (Ni), % 9.0 to 11
0
Silicon (Si), % 0
0 to 0.15
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 38.3 to 45.2
6.0 to 7.0
Residuals, % 0 to 0.5
0 to 0.15