C79600 Nickel Silver vs. AWS E307

C79600 nickel silver belongs to the copper alloys classification, while AWS E307 belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is AWS E307.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 15
34
Poisson's Ratio 0.3
0.28
Shear Modulus, GPa 43
78
Tensile Strength: Ultimate (UTS), MPa 480
660

Thermal Properties

Latent Heat of Fusion, J/g 180
290
Melting Completion (Liquidus), °C 930
1420
Melting Onset (Solidus), °C 880
1370
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 36
15
Thermal Expansion, µm/m-K 21
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
17
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
3.5
Embodied Energy, MJ/kg 57
49
Embodied Water, L/kg 310
160

Common Calculations

Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 12
4.1
Thermal Shock Resistance, points 15
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.040 to 0.14
Chromium (Cr), % 0
18 to 21.5
Copper (Cu), % 43.5 to 46.5
0 to 0.75
Iron (Fe), % 0
59.6 to 69.2
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
3.3 to 4.8
Molybdenum (Mo), % 0
0.5 to 1.5
Nickel (Ni), % 9.0 to 11
9.0 to 10.7
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0