C79600 Nickel Silver vs. EN 1.0644 Steel

C79600 nickel silver belongs to the copper alloys classification, while EN 1.0644 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is EN 1.0644 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 15
17
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 43
73
Shear Strength, MPa 290
420
Tensile Strength: Ultimate (UTS), MPa 480
690
Tensile Strength: Yield (Proof), MPa 300
570

Thermal Properties

Latent Heat of Fusion, J/g 180
250
Maximum Temperature: Mechanical, °C 130
400
Melting Completion (Liquidus), °C 930
1460
Melting Onset (Solidus), °C 880
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 36
47
Thermal Expansion, µm/m-K 21
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.4
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.8
Embodied Energy, MJ/kg 57
24
Embodied Water, L/kg 310
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
110
Resilience: Unit (Modulus of Resilience), kJ/m3 400
870
Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 15
22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.010 to 0.050
Carbon (C), % 0
0.16 to 0.22
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 43.5 to 46.5
0 to 0.3
Iron (Fe), % 0
96.1 to 98.4
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
1.3 to 1.7
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 9.0 to 11
0 to 0.4
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.1 to 0.5
Sulfur (S), % 0
0 to 0.035
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0.080 to 0.15
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0