C79600 Nickel Silver vs. EN 1.1127 Steel

C79600 nickel silver belongs to the copper alloys classification, while EN 1.1127 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is EN 1.1127 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 15
14 to 25
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 43
73
Shear Strength, MPa 290
420 to 480
Tensile Strength: Ultimate (UTS), MPa 480
660 to 790
Tensile Strength: Yield (Proof), MPa 300
410 to 580

Thermal Properties

Latent Heat of Fusion, J/g 180
250
Maximum Temperature: Mechanical, °C 130
400
Melting Completion (Liquidus), °C 930
1460
Melting Onset (Solidus), °C 880
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 36
49
Thermal Expansion, µm/m-K 21
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.5
Embodied Energy, MJ/kg 57
19
Embodied Water, L/kg 310
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
90 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 400
440 to 880
Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 17
23 to 28
Strength to Weight: Bending, points 17
22 to 24
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 15
21 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.34 to 0.42
Chromium (Cr), % 0
0 to 0.4
Copper (Cu), % 43.5 to 46.5
0
Iron (Fe), % 0
96.6 to 98.1
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
1.4 to 1.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 9.0 to 11
0 to 0.4
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.035
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0